Add 1.0% nano-SiC to Mo powder, mix it by planetary ball mill to make it evenly distributed, the ball mill speed is 350 r/min, then press and shape it and sinter it in hydrogen atmosphere furnace at 1600℃, adopt HVS-1000 micro hardness tester, grind and polish the specimen before the test, and ensure the top and bottom surface of the sample is parallel, all the test pressure is 1.0 kg, holding pressure All the test pressure is 1.0 kg, holding time is 10 s. The flat surface of the specimen is selected to measure the hardness, and the instrument used for density test is MZ-Q300 type high-precision powder metallurgy specific gravity meter, and the actual density and relative density of the sintered body can be introduced through the principle of Archimedes' drainage method.