对通过粉末冶金制备的316不锈钢进行了室温拉伸性能的检测。其中，21B0068-T-D-CL-01和21B0068-T-D-CL-02试样的平均屈服强度为240 MPa，平均抗拉强度为575 MPa，平均断面收缩率为43.5%；21B0068-T-D-CL-03和21B0068-T-D-CL-04试样的平均屈服强度为297 MPa，平均抗拉强度为550 MPa，平均断面收缩率为62.5%；21B0068-T-D-CL-05和21B0068-T-D-CL-06试样的平均屈服强度为280 MPa，平均抗拉强度为599 MPa，平均断面收缩率为52.5%。

The tensile properties of 316 stainless steel by powder metallurgy at room temperature were tested. Among them, the average yield strength of 21B0068-T-D-CL-01 and 21B0068-T-D-CL-02 specimens is 240 MPa, the average tensile strength is 575 MPa, and the average section shrinkage is 43.5%; The average yield strength of 21B0068-T-D-CL-03 and 21B0068-T-D-CL-04 specimens is 297 MPa, the average tensile strength is 550 MPa, and the average section shrinkage is 62.5%; The average yield strength of 21B0068-T-D-CL-05 and 21B0068-T-D-CL-06 specimens is 280 MPa, the average tensile strength is 599 MPa, and the average section shrinkage is 52.5%.