GH984G不同磷含量锻态合金及其热变形至真应变为0.69时的孪晶分布图 (a) 锻态合金,(b) 950 °C / 0.01 s-1,(c) 950 °C / 1.0 s-1,(d) 1150 °C / 0.01 s-1,(e) 1150 °C / 1.0 s-1
The twin boundaries in 0P, 0.02P and 0.08P alloys after forging (a) and isothermal compression at 950 °C / 0.01 s-1 (b), 950 °C / 1.0 s-1 (c), 1150 °C / 0.01 s-1 (d) and 1150 °C / 1.0 s-1 (e) with the true strain of 0.69.