| 分析测试报告 |
GH984G标态长期时效合金的700 °C拉伸断口形貌 |
The tensile fracture at 700 °C in alloys after standard heat treatment and thermal exposure |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G合金的700 °C拉伸断口附近纵截面形貌 |
The morphologies of longitudinal section near the tensile fracture surface at 700 °C in GH984G |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G合金700 °C时效10000 h后磷元素的偏析 |
The segregation of phosphorus in the alloys after thermal exposure at 700 °C for 10000 h |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G合金700 °C拉伸过程位错与γ′的交互作用 |
The interaction between dislocations and γ′ particles during 700 °C tensile test |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G合金的室温冲击断口形貌 |
The impact fracture morphologies at room temperature |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G合金室温冲击断口附近纵截面形貌 |
The longitudinal section morphologies of impact fracture at room temperature |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G合金冲击断口纵截面的局部取向差图 |
The local misorientation maps of the longitudinal section near impact fracture |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G冲击断口附近纵截面位错密度随时效时间的变化 |
The change of dislocation density with the thermal exposure time in the longitudinal section |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G标态合金在700℃/400 MPa下的蠕变曲线 |
The creep curves of the standard heat treatment alloys at 700 °C / 400 MPa |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |
| 分析测试报告 |
GH984G标态合金700°C/400 MPa蠕变断口形貌 |
The creep fracture morphologies at 700 °C / 400 MPa in standard heat treatment |
先进超超临界锅炉高温弯管和铸锻件-GH984G铁镍基耐热合金锻件研制数据集 |
2021-07-13 |